Monel 400 Uns N04400 W.Nr. 2.4360 Ak 2.4361
Konpozisyon chimik
| Alyaj | eleman | C | Si | Mn | S | Ni | Fe | Cu |
| Monel 400 | Min | 63.0 | 28.0 | |||||
| Max | 0.3 | 0.5 | 2.0 | 0.024 | 2.5 | 34.0 |
Pwopriyete mekanik
| Estati Aolly | Fòs rupture Rm Mpa Min | Sede fòs RP 0. 2 Mpa Min | Elongasyon A 5% Min |
| Solisyon | 745 | 325 | 40 |
Pwopriyete Fizik
| Estati Aolly | Fòs rupture Rm Mpa Min. | Sede fòs RP 0. 2 Mpa Min. | elongasyon A 5% |
| rkwit | 480 | 170 | 35 |
Estanda
Baton, Bar, Fil ak Forge Stock- ASTM B 164 (Baton, Bar, ak Fil), ASTM B 564 (Forgings)
Plak, fèy ak retire rad sou ou-,ASTM B 127, ASME SB 127
Tiyo & Tib- ASTM B 165 (san tiyo ak tib), ASTM B 725 (soude tiyo), ASTM B 730 (soude tib), ASTM B 751 (soude tib), ASTM B 775 (soude tiyo), ASTM B 829 (san soude tiyo ak Tib)
Pwodwi soude- Filler Metal 60-AWS A5.14/ERNiCu-7;Sodi Electrode 190-AWS A5.11/ENiCu-7.
Karakteristik Monel 400
● Rezistan nan dlo lanmè ak vapè nan tanperati ki wo
● Ekselan rezistans nan dlo saumâtre rapidman ap koule tankou dlo oswa dlo lanmè
● Ekselan rezistans nan krak korozyon estrès nan pifò dlo dous
● Patikilyèman rezistan a asid idroklorik ak fliyorik lè yo de-aere
● Ofri kèk rezistans nan asid idroklorik ak silfirik nan tanperati modès ak konsantrasyon, men se raman materyèl chwa pou asid sa yo.
● Ekselan rezistans nan sèl net ak alkalin
● Rezistans nan klori pwovoke estrès korozyon krak
● Bon pwopriyete mekanik soti nan tanperati anba zewo jiska 1020 ° F
● Segondè rezistans nan alkali